HẠT NHỰA PA615%GF (Trung Quốc)

  • PA6 GF15
Liên hệ

Mã sản phẩm: PA6 BKV15H2

Chống Cháy: HB

Sợi thủy tinh: Sợi Thủy Tinh 15%

Màu sắc: Tự nhiên

Xuất Xứ: Trung Quốc

Hãng sản xuất: LANXESS

Dowload bảng Spec Tại đây.

Trung Quốc

Hạt nhựa PA6 BKV15 - Hạt nhựa PA6 15%GF - PA6 15%GF - PA6 Sợi thủy tinh

Hạt nhựa PA6 BKV15 - Hạt nhựa PA6 15%GF - PA6 15%GF - PA6 Sợi thủy tinh

Hạt nhựa PA6 BKV15 - Hạt nhựa PA6 15%GF - PA6 15%GF - PA6 Sợi thủy tinh 

 30% Glass fiber reinforced; injection molding grade ISO Shortname: ISO 1874-PA 6, GR, 14-100, GF30

 

Property

Test Condition

Unit

Standard

guide value

d.a.m.

 

 

 

 

 

cond.

 

Rheological properties

 

 

 

 

 

 

C Melt volume-flow rate

260 °C; 5 kg

cm³/(10 min)

ISO 1133-1

14

 

 

Molding shrinkage, parallel

150x105x3; 280 °C / MT

80 °C; 500 bar

%

acc. ISO 2577

0.16

 

 

Molding shrinkage, transverse

150x105x3; 280 °C / MT

80 °C; 500 bar

%

acc. ISO 2577

0.82

 

 

Post- shrinkage, parallel

150x105x3; 120 °C; 4 h

%

acc. ISO 2577

0.03

 

 

Post- shrinkage, transverse

150x105x3; 120 °C; 4 h

%

acc. ISO 2577

0.12

 

 

C Molding shrinkage, parallel

60x60x2; 280 °C / MT 80

°C; 600 bar

%

ISO 294-4

0.25

 

 

C Molding shrinkage, transverse

60x60x2; 280 °C / MT 80

°C; 600 bar

%

ISO 294-4

0.75

 

 

Post- shrinkage, parallel

60x60x2; 120 °C; 4 h

%

ISO 294-4

0.05

 

 

Post- shrinkage, transverse

60x60x2; 120 °C; 4 h

%

ISO 294-4

0.1

 

 

Mechanical properties (23 °C/50 % r. h.)

 

 

 

 

 

 

C Tensile modulus

1 mm/min

MPa

ISO 527-1,-2

9800

 

6100

C Tensile Stress at break

5 mm/min

MPa

ISO 527-1,-2

170

 

105

C Tensile Strain at break

5 mm/min

%

ISO 527-1,-2

3.0

 

6.0

C Tensile creep modulus

1 h

MPa

ISO 899-1

 

 

5100

C Tensile creep modulus

1000 h

MPa

ISO 899-1

 

 

4100

C Charpy impact strength

23 °C

kJ/m²

ISO 179-1eU

80

 

95

C Charpy impact strength

-30 °C

kJ/m²

ISO 179-1eU

70

 

70

C Charpy notched impact strength

23 °C

kJ/m²

ISO 179-1eA

12

 

20

C Charpy notched impact strength

-30 °C

kJ/m²

ISO 179-1eA

10

 

10

Izod impact strength

23 °C

kJ/m²

ISO 180-1U

75

 

80

Izod impact strength

-30 °C

kJ/m²

ISO 180-1U

60

 

70

Izod notched impact strength

23 °C

kJ/m²

ISO 180-1A

13

 

20

Izod notched impact strength

-30 °C

kJ/m²

ISO 180-1A

10

 

10

Flexural modulus

2 mm/min

MPa

ISO 178-A

8600

 

5100

Flexural strength

2 mm/min

MPa

ISO 178-A

275

 

170

Flexural strain at flexural strength

2 mm/min

%

ISO 178-A

4.0

 

6.0

Flexural stress at 3.5 % strain

2 mm/min

MPa

ISO 178-A

 

 

145

C Puncture maximum force

23 °C

N

ISO 6603-2

1071

 

 

C Puncture maximum force

-30 °C

N

ISO 6603-2

950

 

 

C Puncture energy

23 °C

J

ISO 6603-2

8

 

14

C Puncture energy

-30 °C

J

ISO 6603-2

6

 

5

Ball indentation hardness

 

N/mm²

ISO 2039-1

210

 

100

 

Property

Test Condition

Unit

Standard                guide

 

 

 

 

value

d.a.m.

 

 

cond.

 

Thermal properties

 

 

 

 

 

 

C Melting temperature

10 °C/min

°C

ISO 11357-1,-3

220

 

 

C Temperature of deflection under load

1.80 MPa

°C

ISO 75-1,-2

200

 

 

C Temperature of deflection under load

0.45 MPa

°C

ISO 75-1,-2

215

 

 

Vicat softening temperature

50 N; 120 °C/h

°C

ISO 306

> 200

 

 

C Coefficient of linear thermal expansion, parallel

23 to 55 °C

10-4/K

ISO 11359-1,-2

0.2

 

 

C Coefficient of linear thermal expansion, transverse

23 to 55 °C

10-4/K

ISO 11359-1,-2

0.8

 

 

C Burning behavior UL 94

1.5 mm

Class

UL 94

HB

 

 

C Burning behavior UL 94

0.75 mm

Class

UL 94

HB

 

 

C Oxygen index

Method A

%

ISO 4589-2

22

 

 

Glow wire test (GWFI)

2.0 mm

°C

IEC 60695-2-12

600

 

 

Burning behavior US-FMVSS302

>=1.0 mm

 

ISO 3795

passed

 

 

C Vicat softening temperature

50 N; 50 °C/h

°C

ISO 306

200

 

 

Electrical properties (23 °C/50 % r. h.)

 

 

 

 

 

 

C Relative permittivity

100 Hz

-

IEC 60250

4.0

 

10

C Relative permittivity

1 MHz

-

IEC 60250

4.0

 

5.0

C Dissipation factor                                                          100 Hz                                 10-4                                                                    IEC 60250

50

2000

C Dissipation factor                                                          1 MHz                                  10-4                                                                    IEC 60250

150

1200

C Volume resistivity

 

Ohm·m

IEC 60093

1E13

1E10

C Surface resistivity

 

Ohm

IEC 60093

1E14

1E12

C Electric strength

1 mm

kV/mm

IEC 60243-1

40

35

C Comparative tracking index CTI

Solution A

Rating

IEC 60112

600

 

Comparative tracking index CTI M

Solution B

Rating

IEC 60112

400 M

 

Other properties (23 °C)

 

 

 

 

 

C Water absorption (Saturation value)

Water at 23 °C

%

ISO 62

7.0

 

C Water absorption (Equilibrium value)

23 °C; 50 % RH

%

ISO 62

2.1

 

C Density

 

kg/m³

ISO 1183

1360

 

Bulk density

 

kg/m³

ISO 60

700

 

Processing conditions for test specimens

 

 

 

 

 

C Injection molding-Melt temperature

 

°C

ISO 294

280

 

C Injection molding-Mold temperature

 

°C

ISO 294

80

 

Processing recommendations

 

 

 

 

 

Drying temperature dry air dryer

 

°C

-

80

 

Drying time dry air dryer

 

h

-

2-6

 

Residual moisture content

 

%

Acc. to Karl Fischer

0.03-0.12

 

Melt temperature (Tmin - Tmax)

 

°C

-

270-290

 

Mold temperature

 

°C

-

80-120

 

 Hạt nhựa PA6 sợi thủy tinh làm tăng độ cứng và định hình sản phẩm tốt hơn

 Hạt nhựa PA6 15%GF làm tăng độ cứng và định hình sản phẩm tốt hơn

 PA6 15%GF làm tăng độ cứng và định hình sản phẩm tốt hơn

Hạt nhựa PA6 BKV15 - Hạt nhựa PA6 15%GF - PA6 15%GF - PA6 Sợi thủy tinh

Hạt nhựa PA6 BKV15 - Hạt nhựa PA6 15%GF - PA6 15%GF - PA6 Sợi thủy tinh

Hạt nhựa PA6 BKV15 - Hạt nhựa PA6 15%GF - PA6 15%GF - PA6 Sợi thủy tinh

- 0% Hạt nhựa nguyên sinh PA66 30%GF

Hạt nhựa nguyên sinh PA66 30%GF

Rated 5.00 out of 5

Mã sản phẩm:

PA66 30%GF

Chống cháy:

HB

Sợi thủy tinh

(Gia cường):

30% Sợi thủy tinh

Màu sắc:

Tự nhiên

Back

Xuất xứ:

Việt Nam

Hãng sản xuất:

RANDOM

 DOWLOAD BẢNG THÔNG SỐ KỸ THUẬT TẠI ĐÂY!

Mua hàng
- 0% Hạt nhựa nguyên sinh PA66 21SPF

Hạt nhựa nguyên sinh PA66 21SPF

Rated 5.00 out of 5

THÔNG SỐ KỸ THUẬT

Hãng sản xuất: ASCEND

Xuất xứ: CHINA

Bảng Spec Dowload tại đây

Mua hàng